| 中文论文题目: |
具有高中孔率的活性炭在基于离子液体作电解液的超级电容器中的物理和电化学表征
|
| 英文论文题目: |
Physical and electrochemical characterization of activated carbons with high mesoporous ratio for supercapacitors based on ionic liquid as the electrolyte
|
| 论文题目英文: |
|
| 作者: |
李开喜
|
| 论文出处: |
|
| 刊物名称: |
Journal of Solid State Electrochemistry
|
| 年: |
2011
|
| 卷: |
15 |
| 期: |
3 |
| 页: |
607 |
| 联系作者: |
李开喜 |
| 收录类别: |
|
| 影响因子: |
2.234
|
| 摘要: |
A series of activated carbons with high mesoporous ratio were prepared by KOH reactivation based on activated carbon as the precursor. As the KOH/AC mass ratio was increased to 4:1, the mesoporous ratio increases from 60% to 76%, and the average pore size from 2.23 to 3.14 nm. Moreover, the specific capacitance for the activated carbon in ionic liquid 1-ethyl-3-methylmidazolium tetrafluoroborate ([EMIm]BF(4)) can reach the maximum value of 189 F g(-1) (8.0 mu F cm(-2)). In addition, the decrease of specific capacitance for activated carbons by KOH reactivation with current density increase shows two regimes, suggesting that activated carbons with high mesoporous ratio are much fit for charge-discharge at larger current density. |
| 英文摘要: |
|
| 外单位作者单位: |
|
| 备注: |
|
关闭窗口 |
|
|
|