Preparation and characterization of a new biomedical Mg–Zn–Ca alloy
|
| 论文题目英文: |
|
| 作者: |
孙宇 *张保平 王银 耿林 焦晓辉
|
| 论文出处: |
|
| 刊物名称: |
Materials & Design
|
| 年: |
2012
|
| 卷: |
34 |
| 期: |
|
| 页: |
58 |
| 联系作者: |
孙宇 *张保平 王银 耿林 焦晓辉 |
| 收录类别: |
|
| 影响因子: |
2.200
|
| 摘要: |
In this paper, the mechanical properties, in vitro degrades and cytotoxicity of？Mg–4.0Zn–0.2Ca？alloy？were studied. The extruded？Mg–4.0Zn–0.2Ca？alloy？exhibited peak strength of 297？MPa, yield strength of 240？Mpa, elongation of 21.3% and elastic modulus of 45？GPa, respectively. After 30？days immersion in SBF solutions, the values of the yield strength, the ultimate tensile strength, the elongation and the elastic modulus of the？alloy？were degraded to 160？MPa, 220？MPa, 8.5% and 40？GPa respectively. It is still enough for bone fixed. The in vitro corrosion test in the simulated body fluid (SBF) revealed that the addition of？Znand？Ca？into？Mg？matrix could enhance the corrosion potential and reduced the degradation rate. In vitro cytotoxicity of the？alloy？was disclosed that？Mg–4.0Zn–0.2Ca？alloy？has suitable biocompatibility. |
| 英文摘要: |
|
| 外单位作者单位: |
|
| 备注: |
|
关闭窗口 |
|
|
|